ASTM A182 F55
F55
X2CrNiMoCuWN25 7 4
1.4501
UNS S32760
ASTM A182/A182M
Zeron 100
Seacol 760
Stainless Steel
Base Element Fe (Iron)
| Element | Min | Max |
|---|---|---|
| C (Carbon) | 0.03% | |
| Cr (Chromium) | 24% | 26% |
| Cu (Copper) | 0.5% | 1% |
| Mn (manganese) | 1% | |
| Mo (Molybdenum) | 3% | 4% |
| N (Nitrogen) | 0.2% | 0.3% |
| Ni (Nickel) | 6% | 8% |
| P (Phosphorus) | 0.03% | |
| S (Sulphur) | 0.01% | |
| Si(Silicon) | 1% | |
| W(Tungsten) | 0.5% | 1% |
| Mechanical Property | Min | Max |
|---|---|---|
| Ultimate Tensile strength (UTS) | 750 MPa | 895 MPa |
| Yield Strength | 550 Mpa | |
| Elongation | 25% | |
| Reduction of Area | 45% | |
| Gauge Length | A50mm |
Heat Treatment; After hot working , forgings shall be cooled to a temperature below 538 degrees CEntigrade prior to heat treating.
Solution treat and quench. Austenizing/Solutioning Temperature, 1100-1140 min degrees Centigrade.
Uses
Bolting
Used in piping components for use in pressure systems. Including flanges, fittings, valves and other similar parts.